Diamas est praestans material crystallinum Raman, cum maxima translatione frequentiae Raman 1332.3 cm -1inter materiales crystallinos notos, et latitudo Raman gain aestimationis circiter 1.5 cm -1ad temperaturam ambientalem. Capacitas ultra celeris diffusionis caloris permittit cristallis diamatis servare altam Raman gain inmutatam sub operatione altae potentiae et consequi exitium laseris optimae qualitatis.
| Proprietates | |
| Index Refractionis (1064nm) | 2.392 |
| Index Refractionis (600nm) | 2.415 |
| Transmissio (1064nm) | ＞68% |
| Transmissio (8μm-25μm) | ＞70% |
| Scelerisque Conductivity | >2000 W/mK |
| Processus Norma | |
| Orientatio Crystallographica | 100 110 111 |
| Miscut pro Orientatione Faciei Principalis | ±3° |
| Communis Magnitudo Productus |
2mm×2mm×6mm 2mm×2mm×7mm 2mm×2mm×9mm 4mm×4mm×6mm 4mm×4mm×7mm 4mm×4mm×9mm |
| Tolerantia Transversa | ±0.05mm |
| Tolerantia Crassitiei | ±0.1mm |
| Parallelismus | ＜2′ |
| Superficiem asperitatem | ＜10nm |
| Incisio Marginis | Laser sectionem |
| Comparatum ad Alios Crystallum Raman cum Alto Guadagno | ||||
| Unicus Crystallinus CVD Diamas | KGW KGD(WO 4)2 | YVO 4 | BA(NO 3)2 | |
| Raman Guadagnus(g) | 15 | 4 | 5 | 11 |
| Raman Translatio Frequens ∆λ cm -1 | 1332 | 901 | 892 | 1047 |
| Crystallum Longitudo(L)mm | 8 | 25 | 25 | 25 |
| Conductivitas Thermica (k)Wm -1K -1 | >2000 | 5 | 5.2 | 1.2 |
| Raman Figura Meriti | 1440 | 3 | 20 | 1 |
Albi et colorati in vario modo diamantes culti in laboratorio in diversis dimensionibus et formis;
Offerti ut lapides certificati/non certificati, pares congruentes, et fasciculi calibrati.